.: ORİJİNAL ARAŞTIRMA
Farklı Bitirme ve Parlatma Sistemlerinin ''Bulk Fill'' Kompozit Rezinlerin Yüzey Pürüzlülüğüne Etkisi
Effect of Different Finishing and Polishing Systems on Surface Roughness of Bulk Fill Composite Resin
Turkiye Klinikleri J Dental Sci. 2021;27(2):280-5
doi: 10.5336/dentalsci.2020-74864
Makale Dili: TR
Tam Metin
Ücretsiz Erişim
ÖZET
Amaç: Bu in vitro çalışmanın amacı, farklı bitirme ve parlatma sistemle- rinin farklı tipteki kompozit rezinlerin yüzey pürüzlülüğü üzerine etkisini değer- lendirmektir. Gereç ve Yöntemler: Bu çalışmada, 3 farklı tipte 'bulk fill' kompozit rezin kullanıldı; SonicFill, Fill-Up, Estelite Bulk Fill Flow. Toplam 72 adet kompozit disk hazırlandı (n=24). Örnekler, her alt grupta 8 örnek olacak şekilde uygulanan parlatma yöntemine göre rastgele 3 alt gruba ayrıldı. Kontrol grubundaki örneklere herhangi bir işlem uygulanmadı, diğer gruplardaki örneklere ise iki aşamalı Kenda ve üç aşamalı OptiDisc parlatma sistemleri uygulandı. Örneklerin yüzey pürüzlülükleri profilometre kullanılarak ölçüldü. İstatistiksel analiz tek yönlü ANOVA ve 'post hoc' testleri kullanılarak yapıldı (p=0,05). Bulgular: Bütün gruplarda, en düşük pürüzlülük değerleri kontrol grubunda ölçüldü ve Estelite Bulk Fill Flow, SonicFill, Fill-Up grupları arasında anlamlı bir farklılık bulunmadı. OptiDisc uygulanan grupta, SonicFill, Estelite Bulk Fill Flow ve FillUp grupları birbirlerinden anlamlı düzeyde farklı bulundu. Polisaj lastiği uygulanan grupta, Estelite Bulk Fill Flow ve SonicFill gruplarının pürüzlülük değerleri benzer, Fill-Up grubunun pürüzlülük değeri ise daha düşük bulundu. Bitim ve polisaj uygulanan gruplar arasında, en az pürüzlülük değeri OptiDisc polisaj sistemi uygulanan Estelite Bulk Fill Flow grubu gösterdi. Sonuç: Kompozit rezinlerin polisajında uygulanan tek aşamalı veya çok aşamalı sistemler, yüzey pürüzlülüğü açısından farklılık gösterebilir. Yapılan bu in vitro çalışmanın sınırlamaları dâhilinde kompozit rezin tipinden bağımsız olarak diskle yapılan parlatma işlemleri ile en düşük pürüzlülük değerleri elde edilmiştir.
Anahtar Kelimeler: Bitirme ve polisaj; ''bulk fill'' kompozit; yüzey pürüzlülük
Amaç: Bu in vitro çalışmanın amacı, farklı bitirme ve parlatma sistemle- rinin farklı tipteki kompozit rezinlerin yüzey pürüzlülüğü üzerine etkisini değer- lendirmektir. Gereç ve Yöntemler: Bu çalışmada, 3 farklı tipte 'bulk fill' kompozit rezin kullanıldı; SonicFill, Fill-Up, Estelite Bulk Fill Flow. Toplam 72 adet kompozit disk hazırlandı (n=24). Örnekler, her alt grupta 8 örnek olacak şekilde uygulanan parlatma yöntemine göre rastgele 3 alt gruba ayrıldı. Kontrol grubundaki örneklere herhangi bir işlem uygulanmadı, diğer gruplardaki örneklere ise iki aşamalı Kenda ve üç aşamalı OptiDisc parlatma sistemleri uygulandı. Örneklerin yüzey pürüzlülükleri profilometre kullanılarak ölçüldü. İstatistiksel analiz tek yönlü ANOVA ve 'post hoc' testleri kullanılarak yapıldı (p=0,05). Bulgular: Bütün gruplarda, en düşük pürüzlülük değerleri kontrol grubunda ölçüldü ve Estelite Bulk Fill Flow, SonicFill, Fill-Up grupları arasında anlamlı bir farklılık bulunmadı. OptiDisc uygulanan grupta, SonicFill, Estelite Bulk Fill Flow ve FillUp grupları birbirlerinden anlamlı düzeyde farklı bulundu. Polisaj lastiği uygulanan grupta, Estelite Bulk Fill Flow ve SonicFill gruplarının pürüzlülük değerleri benzer, Fill-Up grubunun pürüzlülük değeri ise daha düşük bulundu. Bitim ve polisaj uygulanan gruplar arasında, en az pürüzlülük değeri OptiDisc polisaj sistemi uygulanan Estelite Bulk Fill Flow grubu gösterdi. Sonuç: Kompozit rezinlerin polisajında uygulanan tek aşamalı veya çok aşamalı sistemler, yüzey pürüzlülüğü açısından farklılık gösterebilir. Yapılan bu in vitro çalışmanın sınırlamaları dâhilinde kompozit rezin tipinden bağımsız olarak diskle yapılan parlatma işlemleri ile en düşük pürüzlülük değerleri elde edilmiştir.
Anahtar Kelimeler: Bitirme ve polisaj; ''bulk fill'' kompozit; yüzey pürüzlülük
ABSTRACT
Objective: The purpose of this in vitro study was to evaluate the effect of different finishing and polishing systems on the surface roughness of different types of composite resins. Material and Methods: In this study, 3 different types of bulk fill composite resin were used; SonicFill, Fill-Up, Estelite Bulk Fill Flow. A total of 72 composite discs were prepared (n=24). The samples were randomly divided into 3 subgroups according to the polishing systems with 8 samples in each subgroup. Samples in the control group was left untreated, and samples in the remaining groups were subjected to two stage Kenda and three stage OptiDisc polishing systems. The surface roughness of the samples was measured using a profilometer. Statistical analysis was performed using one-way ANOVA and post hoc tests. Results: In all groups, the lowest roughness values were measured in the control group and no significant difference was found between Estelite Bulk Fill Flow, SonicFill, Fill-Up groups. In the OptiDisc applied group, SonicFill, Estelite Bulk Fill Flow and Fill-Up groups were found to be significantly different from each other. In the polishing rubber group, the roughness values of Estelite Bulk Fill Flow and SonicFill groups were similar, while the roughness value of Fill-Up group was lower. Among the finishing and polishing groups the Estelite Bulk Fill Flow group with the OptiDisc polishing system showed the least roughness value. Conclusion: Single-step or multi-step systems applied in the polishing of composite resins may differ in terms of surface roughness. Within the limitations of this in vitro study, the lowest roughness values were obtained with the polishing processes performed with the disc, regardless of the composite resin type.
Keywords: Finishing and polishing; bulk fill composite; surface roughness
Objective: The purpose of this in vitro study was to evaluate the effect of different finishing and polishing systems on the surface roughness of different types of composite resins. Material and Methods: In this study, 3 different types of bulk fill composite resin were used; SonicFill, Fill-Up, Estelite Bulk Fill Flow. A total of 72 composite discs were prepared (n=24). The samples were randomly divided into 3 subgroups according to the polishing systems with 8 samples in each subgroup. Samples in the control group was left untreated, and samples in the remaining groups were subjected to two stage Kenda and three stage OptiDisc polishing systems. The surface roughness of the samples was measured using a profilometer. Statistical analysis was performed using one-way ANOVA and post hoc tests. Results: In all groups, the lowest roughness values were measured in the control group and no significant difference was found between Estelite Bulk Fill Flow, SonicFill, Fill-Up groups. In the OptiDisc applied group, SonicFill, Estelite Bulk Fill Flow and Fill-Up groups were found to be significantly different from each other. In the polishing rubber group, the roughness values of Estelite Bulk Fill Flow and SonicFill groups were similar, while the roughness value of Fill-Up group was lower. Among the finishing and polishing groups the Estelite Bulk Fill Flow group with the OptiDisc polishing system showed the least roughness value. Conclusion: Single-step or multi-step systems applied in the polishing of composite resins may differ in terms of surface roughness. Within the limitations of this in vitro study, the lowest roughness values were obtained with the polishing processes performed with the disc, regardless of the composite resin type.
Keywords: Finishing and polishing; bulk fill composite; surface roughness
REFERANSLAR:
- Yap AU, Yap SH, Teo CK, Ng JJ. Finishing/polishing of composite and compomer restoratives: effectiveness of one-step systems. Oper Dent. 2004;29(3):275-9. [PubMed]
- Ilie N, Bucuta S, Draenert M. Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance. Oper Dent. 2013;38(6):618-25. [Crossref] [PubMed]
- Chesterman J, Jowett A, Gallacher A, Nixon P. Bulk-fill resin-based composite restorative materials: a review. Br Dent J. 2017;222(5):337-44. [Crossref] [PubMed]
- Amal A, Sakrana E, Abouelatta OB, Matsumura H, Tanoue HKN. Surface roughness evaluation of polished composite using three dimension profilometry. Int Chin J Dent 2004;4:85-91. [Link]
- Quirynen M, Bollen CM. The influence of surface roughness and surface-free energy on supra- and subgingival plaque formation in man. A review of the literature. J Clin Periodontol. 1995;22(1):1-14. [Crossref] [PubMed]
- Kelsey WP, Latta MA, Shaddy RS, Stanislav CM. Physical properties of three packable resin-composite restorative materials. Oper Dent. 2000;25(4):331-5. [PubMed]
- Roeder LB, Tate WH, Powers JM. Effect of finishing and polishing procedures on the surface roughness of packable composites. Oper Dent. 2000;25(6):534-43. [PubMed]
- Toledano M, De La Torre FJ, Osorio R. Evaluation of two polishing methods for resin composites. Am J Dent. 1994;7:328-30.
- Ölmez A, Kisbet S. [Advancements in finishing and polishing procedures for composite resin restorations]. Acta Odontolojica Turcica. 2013;30(2):115-22. [Link]
- Barbosa SH, Zanata RL, Navarro MF, Nunes OB. Effect of different finishing and polishing techniques on the surface roughness of microfilled, hybrid and packable composite resins. Braz Dent J. 2005;16(1):39-44. [Crossref] [PubMed]
- Gupta T, Mohan B, Lakshmi Narayanan LL. Profilometric analysis of microfilled resin using five different polishing systems. J Conserv Dent. 2002;5(3):110-3. [Link]
- Uppal M, Ganesh A, Balagopal S, Kaur G. Profilometric analysis of two composite resins' surface repolished after tooth brush abrasion with three polishing systems. J Conserv Dent. 2013;16(4):309-13. [Crossref] [PubMed] [PMC]
- Bilgili D, Dündar A, Barutçugil Ç, Öcal İB. [Effect of different polishing system on surface roughness of composite resins] Yeditepe Üniversitesi Diş Hekimliği Fakültesi Dergisi 2020;16(2):147-53. [Crossref]
- Ferraris F, Conti A. Superficial roughness on composite surface, composite enamel and composite dentin junctions after different finishing and polishing procedures. Part I: roughness after treatments with tungsten carbide vs diamond burs. Int J Esthet Dent. 2014;9(1):70-89. [PubMed]
- Corsalini M, Boccaccio A, Lamberti L, Pappalettere C, Catapano S, Carossa S, et al. Analysis of the performance of a standardized method for the polishing of methacrylic resins. Open Dent J. 2009;3:233-40. [Crossref] [PubMed] [PMC]
- Başeren M. Surface roughness of nanofill and nanohybrid composite resin and ormocer-based tooth-colored restorative materials after several finishing and polishing procedures. J Biomater Appl. 2004;19(2):121-34. [Crossref] [PubMed]
- Korkmaz Y, Ozel E, Attar N, Aksoy G. The influence of one-step polishing systems on the surface roughness and microhardness of nanocomposites. Oper Dent. 2008;33(1):44-50. [Crossref] [PubMed]
- Marigo L, Rizzi M, La Torre G, Rumi G. 3-D surface profile analysis: different finishing methods for resin composites. Oper Dent. 2001;26(6):562-8. [PubMed]
- Daud A, Gray G, Lynch CD, Wilson NHF, Blum IR. A randomised controlled study on the use of finishing and polishing systems on different resin composites using 3D contact optical profilometry and scanning electron microscopy. J Dent. 2018;71:25-30. [Crossref] [PubMed]
- Lu H, Roeder LB, Lei L, Powers JM. Effect of surface roughness on stain resistance of dental resin composites. J Esthet Restor Dent. 2005;17(2):102-8; discussion 109. [Crossref] [PubMed]
- Reis AF, Giannini M, Lovadino JR, Ambrosano GM. Effects of various finishing systems on the surface roughness and staining susceptibility of packable composite resins. Dent Mater. 2003;19(1):12-8. [Crossref] [PubMed]
- Rodway Mackert J. Physical properties and Biocompatibility. O'Brien WJ, ed. Dental Materials and Their Selection. 4th ed. Michigan: Quintessence Publishing Co.; 2008. p.12-23.
- Patel SB, Gordan VV, Barrett AA, Shen C. The effect of surface finishing and storage solutions on the color stability of resin-based composites. J Am Dent Assoc. 2004;135(5):587-94; quiz 654. [Crossref] [PubMed]
.: İşlem Listesi